WOLFRAM INDUSTRIE made in Germany

wolfram-industrie
TRIAMET® A12

非鉄金属の鋳造工程において湯口や金型部に磨耗や亀裂が発生します。金型部品が非鉄金属の侵食により製品保証が出来なくなります。また、金型の補修及び補修期間の生産ロスが発生します。多大なメンテナンス費用と生産ロスの改善は不可欠です。
WOLFRAM INDUSTRY TRIAMET® A12は融解非鉄金属に対して良好な耐食性と温度変化中でも安定性があります。合金化による侵食は極めて低く離形性が良く、使用寿命と製品品質は大幅に向上します。
特徴はタングステンを主成分としています。また、熱膨張率が金型部品に近く肉盛後においても親和性があります。

特性表

Technical Specification TRIAMET® A12 Hot Work Steel1.2343
Hardness 硬度 310±20 HV10 380-480 HV10
DENSITY 密度 12.0±0.1 g/㎤ 8.0±0.1 g/㎤
Thermal conductivity
熱伝導率
Approx. 48W/m・K 23 W/m・K
Thermal expansion
coefficient (20-800°C)
熱膨張率(20-800°C)
Approx. 10 10-6/K 12.2 10-6/K

Foundries for non-ferrous metals can adapt to increasing quality requirements and added cost pressure by optimising processes. The casting process exhibits considerable potential for savings, in particular in areas which are characterized by the fact that liquid aluminium attacks ladles, guides, and casting tools. The inevitable abrasion in conventional moulds which is due to separating procedures and erosion processes as well as cracking because of thermal fatigue entails both a large maintenance expenditure and a considerable loss of use. In addition, the quality of the cast products is reduced by weldings and displaced material. This can result in a higher susceptibility to corrosion and inadequate surfaces of the cast parts.

The TRIAMET® A material group exhibits high levels of resistance against liquid aluminium and magnesium, high levels of stability during changes in temperature, and a negligibly low tendency for forming alloys. In addition, it forms a natural separating layer. These characteristics allow for drastic improvements of the service lives and the quality of the products. This is due to the special composition of the TRIAMET® A materials. They contain large amounts of tungsten, the metal with the highest melting point, in particular 3,410°C. In combination with the special structure, this characteristic already resulted in 2,000 times longer service lives of centre ejectors, cooling cores, or distributors suitable for producing aluminium rims or cylinder heads. Due to their excellent machinability, the TRIAMET® A materials can easily be used. In addition, the workload of the operating individual is eased because residues can easily be removed from the mould.

納期:○翌日発送、△4日後発送、×無し
サイズ(単位:mm) 単位 価格(税込) 買い物かご
φ1.0 × 500mm 1本 3,200円
納期 ○
数量:
φ1.5 × 500mm 1本 2,700円
納期 ○
数量:
φ3.0 × 500mm 1本 5,400円
納期 △
数量:

●ご注文方法

  • 詳細はこちらからご覧下さい。
  • 個人情報保護のための行動指針
  • ►納 期:翌日発送致します。
  • ►送 料:御負担お願い致します。 運賃一覧表
  • ►お支払:
      ①ヤマトコレクトサービス。費用は324円です。
        ヤマト宅急便で商品と引き換えに商品代金を現金にて集金致します。
      ②お振り込みの場合は送金確認後発送いたします。
        手数料はご負担の程お願い致します。
  • ►消費税:表示金額は含まれます。(総額表示)
  • 通信販売法(訪問販売法)に基づく表記(法令第8条、省令第7条)
    (ネット取引の契約成立前情報提供義務)
page top